Products
- Titanium Tablet
- Carbide Powder
- Nitride Powders
- Hydride Powders
- Silicide Powders
- Ti5Si3 Titanium Silicide
- TaSi2 Tantalum Silicide
- VSi2 Vanadium Silicide
- CrSi2 Chromium Silicide
- HfSi2 Hafnium Silicide
- Mg2Si Magnesium Silicide
- MnSi Manganese Silicide
- MoSi2 Molybdenum Silicide
- NbSi2 Niobium Silicide
- Ni2Si Nickel Silicide
- TiSi2 Titanium Disilicide
- WSi2 Tungsten Silicide
- FeSi2 Ferro Silicide
- ZrSi2 Zirconium Silicide
- Cu5Si Copper Silicide
- CoSi2 Cobalt Silicide
- Yttrium Disilicide,YSi2
- Calcium Silicide,CaSi2
- Boride Powders
- TiB2 Titanium Boride Powder
- TaB2 Tantalum Boride powder
- ZrB2 Zirconium Boride Powder
- VB2 Vanadium Boride Powder
- CaB6 Calcium Boride Powder
- CrB2 Chromium Boride Powder
- CoB Cobalt Boride Powder
- SiB6 Silicon Boride Powder
- HfB2 Hafnium Boride Powder
- AlB2 Aluminum Boride Powder
- MgB2 Magnesium Boride Powder
- MnB2 Manganese Boride Powder
- MoB2 Molybdenum Boride Powder
- NbB2 Niobium Boride Powder
- Ni2B Nickel Boride Powder
- WB2 Tungsten Boride Powder
- MoB Molybdenum Boride powder
- WB Tungsten Boride powder
- FeB Iron Boride powder
- Metal Alloy Powders
- High purity powders
- Max materials
VH2 Vanadium Hydride Powder
Haixin is one of the leading and professional VH2 Vanadium Hydride Powder manufacturers in China. Providing you with good after-sales service and quick delivery, we warmly welcome you to high quality VH2 Vanadium Hydride Powder at the most competitive price with us.
Send Inquiry
Product Description
VH2 Vanadium Hydride Powder
Hydrogenated vanadium
Chinese name: Vanadium hydride
Vanadium hydride
Molecular formula: VH2
Molecular weight: 55.9812
Vanadium hydride (VH2), when the temperature rises from 25 ° C to 200 ° C, the pressure of hydrogen emission will rise sharply from 0.19 mpa (1.9 atmospheric pressure) to 87 mpa (870 atmospheric pressure), which can be said to be an ideal compressor. Vanadium hydride is a transition metal hydride. The elements of scandium, vanadium, chromium, nickel, palladium, lanthanide and actinide in transition metals can form binary compounds with hydrogen.
Properties of vanadium hydride:
(1)VH2 is very unstable. When the temperature is 13℃, its dissociation pressure has reached 1.01×105Pa. Its reaction formula is 2VH2→2VH+H2.
(2)The metal vanadium hydride is a gray metal substance, after the absorption of hydrogen, lattice expansion.
(3) Hydride density is about 6% ~ 10% lower than vanadium metal.
(4) Metal vanadium becomes brittle after absorption of hydrogen. Heated to 600℃ ~ 700℃ in vacuum, the hydride of vanadium is decomposed. With the release of hydrogen, the hardness of vanadium decreases and the plastic property is restored.
(5)It does not interact with water, nor with boiling hydrochloric acid, but is oxidized by nitric acid. Vanadium hydride is used in hydrogen storage alloy, its hydrogen storage capacity is large, is a promising compound.